    Profex Medical Products rietveld refinement analysis profex 4.3
    Overview of β-TCP characteristics: ( a ): ESEM Image HFW 46.6 μm (fracture surface); HV: 10 kV; LFD detector @ 100 Pa; ( b ): µCT of porosity of the β-TCP taken by Scanco Micro-CT 50 at 90 kV, 4 W, 44 µA at a resolution of 2 μm and an integration time of 5000 ms ; ( c ): Pore size distribution; measurements of the Pascal-140 porosimeter (1000 μm–1.4 μm; pressure increase to 0.1 kPa) in blue and the Pascal-440 porosimeter (1.4 μm–1.8 nm; pressure increase to 400 MPa) in purple (Porotec Pascal 140/440, Hofheim, Germany); ( d ): XRD pattern of the TCP (Bruker D8 Advance, Billerica, USA; Bragg-Brentano geometry; Cu anode; secondary graphite monochromator; scintillation counter; 40 kV/40 mA; 1°2-theta/ min; step size 0.02°2theta) and <t>Rietveld</t> Refinement with Profex 4.3
    Rietveld Refinement Analysis Profex 4.3, supplied by Profex Medical Products, used in various techniques. Bioz Stars score: 90/100, based on 1 PubMed citations. ZERO BIAS - scores, article reviews, protocol conditions and more
    https://www.bioz.com/product/rietveld+refinement+analysis+profex+4%2E3/rietveld+refinement+software/pmc11149308-167-9-12
    Average 90 stars, based on 1 article reviews
    rietveld refinement analysis profex 4.3 - by Bioz Stars, 2026-09
    90/100 stars

    Images

    1) Product Images from "Dual release of daptomycin and BMP-2 from a composite of β-TCP ceramic and ADA gelatin"

    Article Title: Dual release of daptomycin and BMP-2 from a composite of β-TCP ceramic and ADA gelatin

    Journal: BMC Biotechnology

    doi: 10.1186/s12896-024-00863-4

    Overview of β-TCP characteristics: ( a ): ESEM Image HFW 46.6 μm (fracture surface); HV: 10 kV; LFD detector @ 100 Pa; ( b ): µCT of porosity of the β-TCP taken by Scanco Micro-CT 50 at 90 kV, 4 W, 44 µA at a resolution of 2 μm and an integration time of 5000 ms ; ( c ): Pore size distribution; measurements of the Pascal-140 porosimeter (1000 μm–1.4 μm; pressure increase to 0.1 kPa) in blue and the Pascal-440 porosimeter (1.4 μm–1.8 nm; pressure increase to 400 MPa) in purple (Porotec Pascal 140/440, Hofheim, Germany); ( d ): XRD pattern of the TCP (Bruker D8 Advance, Billerica, USA; Bragg-Brentano geometry; Cu anode; secondary graphite monochromator; scintillation counter; 40 kV/40 mA; 1°2-theta/ min; step size 0.02°2theta) and Rietveld Refinement with Profex 4.3
    Figure Legend Snippet: Overview of β-TCP characteristics: ( a ): ESEM Image HFW 46.6 μm (fracture surface); HV: 10 kV; LFD detector @ 100 Pa; ( b ): µCT of porosity of the β-TCP taken by Scanco Micro-CT 50 at 90 kV, 4 W, 44 µA at a resolution of 2 μm and an integration time of 5000 ms ; ( c ): Pore size distribution; measurements of the Pascal-140 porosimeter (1000 μm–1.4 μm; pressure increase to 0.1 kPa) in blue and the Pascal-440 porosimeter (1.4 μm–1.8 nm; pressure increase to 400 MPa) in purple (Porotec Pascal 140/440, Hofheim, Germany); ( d ): XRD pattern of the TCP (Bruker D8 Advance, Billerica, USA; Bragg-Brentano geometry; Cu anode; secondary graphite monochromator; scintillation counter; 40 kV/40 mA; 1°2-theta/ min; step size 0.02°2theta) and Rietveld Refinement with Profex 4.3

    Techniques Used: Micro-CT, Pore Size

    Related Articles

    Micro-CT:

    Article Title: Dual release of daptomycin and BMP-2 from a composite of β-TCP ceramic and ADA gelatin
    Article Snippet: EDX shows a Ca/P ratio of 1.48, which identified the sample as β-TCP. .. The XRD measurement confirmed the result with the subsequent Rietveld refinement analysis (Profex 4.3., www.profex.org , Freeware). .. 99.5% β-TCP and traces of calciumpyprophpshate (CPP) from the manufacturi

    Article Title: Alternative Geometries for 3D Bioprinting of Calcium Phosphate Cement as Bone Substitute.
    Article Snippet: The XRD spectra were analyzed using a Rietveld refinement analysis (Profex 4.3). There was no significant difference between the samples with or without incubation in PBS, while 90% HA, 7% α-TCP, and 3% CDHA could be detected (for further information, please see Figure A2 in Appendix A).

    Pore Size:

    Article Title: Dual release of daptomycin and BMP-2 from a composite of β-TCP ceramic and ADA gelatin
    Article Snippet: EDX shows a Ca/P ratio of 1.48, which identified the sample as β-TCP. .. The XRD measurement confirmed the result with the subsequent Rietveld refinement analysis (Profex 4.3., www.profex.org , Freeware). .. 99.5% β-TCP and traces of calciumpyprophpshate (CPP) from the manufacturi

    Article Title: Alternative Geometries for 3D Bioprinting of Calcium Phosphate Cement as Bone Substitute.
    Article Snippet: The XRD spectra were analyzed using a Rietveld refinement analysis (Profex 4.3). There was no significant difference between the samples with or without incubation in PBS, while 90% HA, 7% α-TCP, and 3% CDHA could be detected (for further information, please see Figure A2 in Appendix A).



    Similar Products

    rietveld refinement analysis profex 4.3  (Profex Medical Products)
    90
    Profex Medical Products rietveld refinement analysis profex 4.3
    Overview of β-TCP characteristics: ( a ): ESEM Image HFW 46.6 μm (fracture surface); HV: 10 kV; LFD detector @ 100 Pa; ( b ): µCT of porosity of the β-TCP taken by Scanco Micro-CT 50 at 90 kV, 4 W, 44 µA at a resolution of 2 μm and an integration time of 5000 ms ; ( c ): Pore size distribution; measurements of the Pascal-140 porosimeter (1000 μm–1.4 μm; pressure increase to 0.1 kPa) in blue and the Pascal-440 porosimeter (1.4 μm–1.8 nm; pressure increase to 400 MPa) in purple (Porotec Pascal 140/440, Hofheim, Germany); ( d ): XRD pattern of the TCP (Bruker D8 Advance, Billerica, USA; Bragg-Brentano geometry; Cu anode; secondary graphite monochromator; scintillation counter; 40 kV/40 mA; 1°2-theta/ min; step size 0.02°2theta) and <t>Rietveld</t> Refinement with Profex 4.3
    Rietveld Refinement Analysis Profex 4.3, supplied by Profex Medical Products, used in various techniques. Bioz Stars score: 90/100, based on 1 PubMed citations. ZERO BIAS - scores, article reviews, protocol conditions and more
    https://www.bioz.com/product/rietveld+refinement+analysis+profex+4%2E3/rietveld+refinement+software/pmc11149308-167-9-12
    Average 90 stars, based on 1 article reviews
    rietveld refinement analysis profex 4.3 - by Bioz Stars, 2026-09
    90/100 stars
    		  Buy from Supplier

    Image Search Results


    Overview of β-TCP characteristics: ( a ): ESEM Image HFW 46.6 μm (fracture surface); HV: 10 kV; LFD detector @ 100 Pa; ( b ): µCT of porosity of the β-TCP taken by Scanco Micro-CT 50 at 90 kV, 4 W, 44 µA at a resolution of 2 μm and an integration time of 5000 ms ; ( c ): Pore size distribution; measurements of the Pascal-140 porosimeter (1000 μm–1.4 μm; pressure increase to 0.1 kPa) in blue and the Pascal-440 porosimeter (1.4 μm–1.8 nm; pressure increase to 400 MPa) in purple (Porotec Pascal 140/440, Hofheim, Germany); ( d ): XRD pattern of the TCP (Bruker D8 Advance, Billerica, USA; Bragg-Brentano geometry; Cu anode; secondary graphite monochromator; scintillation counter; 40 kV/40 mA; 1°2-theta/ min; step size 0.02°2theta) and Rietveld Refinement with Profex 4.3

    Journal: BMC Biotechnology

    Article Title: Dual release of daptomycin and BMP-2 from a composite of β-TCP ceramic and ADA gelatin

    doi: 10.1186/s12896-024-00863-4

    Figure Lengend Snippet: Overview of β-TCP characteristics: ( a ): ESEM Image HFW 46.6 μm (fracture surface); HV: 10 kV; LFD detector @ 100 Pa; ( b ): µCT of porosity of the β-TCP taken by Scanco Micro-CT 50 at 90 kV, 4 W, 44 µA at a resolution of 2 μm and an integration time of 5000 ms ; ( c ): Pore size distribution; measurements of the Pascal-140 porosimeter (1000 μm–1.4 μm; pressure increase to 0.1 kPa) in blue and the Pascal-440 porosimeter (1.4 μm–1.8 nm; pressure increase to 400 MPa) in purple (Porotec Pascal 140/440, Hofheim, Germany); ( d ): XRD pattern of the TCP (Bruker D8 Advance, Billerica, USA; Bragg-Brentano geometry; Cu anode; secondary graphite monochromator; scintillation counter; 40 kV/40 mA; 1°2-theta/ min; step size 0.02°2theta) and Rietveld Refinement with Profex 4.3

    Article Snippet: The XRD measurement confirmed the result with the subsequent Rietveld refinement analysis (Profex 4.3., www.profex.org , Freeware).

    Techniques: Micro-CT, Pore Size